In vivo study of novel biodegradable and osteoconductive CaO-SiO2-B2O3 glass-ceramics

Cited 29 time in Web of Science Cited 29 time in Scopus
Authors

Lee, Jae Hyup; Lee, Choon-Ki; Chang, Bong-Soon; Ryu, Hyun-Seung; Seo, Jun-Hyuk; Hong, Kug Sun; Kim, Hwan

Issue Date
2006-01-21
Publisher
John Wiley & Sons
Citation
J Biomed Mater Res A 2006;77:362-369
Keywords
CaO-SiO2-B2O3 glass-ceramicshydroxyapatitetricalcium phosphateosteoconductionbiodegradation
Abstract
To evaluate the possibility of novel CaO-SiO2-B2O3 glass-ceramics (CS10B) as a new bone replacement material, we compared the biodegradation and osteoconduction properties of CS10B, hydroxyapatite (HA), and tricalcium phosphate (TCP). Porous CS10B implants were prepared by the polymer sponge method. L5-6 single-level posterolateral spinal fusions were performed on 30 New Zealand white male rabbits. The animals were divided into three groups by implant material: CS10B, HA, and TCP. Radiographs were performed every 2 weeks. All animals were euthanized 12 weeks after surgery. The ratio of the area occupied by the ceramics by final and initial radiographs was calculated using radiomorphometric analysis. Uniaxial tensile strength was determined from seven cases in each group. The ratio of the area occupied by HA (88.7%+/-16.1%) was significantly higher than the others (p<0.005), and the ratio of the area occupied by CS10B (28.2%+/-9.3%) was significantly lower than those of HA and TCP (37%+/-9.6%, p<0.05). The mean values of the tensile strengths of the CS10B (182.7+/-19.9 N) and HA (191.4+/-33.5 N) were significantly higher (p<0.05) than that of TCP (141.1+/-28.2 N). CS10B had a fusion mass tensile strength similar to that of HA. Histological analysis confirmed that CS10B was well incorporated into the fusion mass. These findings suggest that CS10B is a possible bone replacement material.
ISSN
1549-3296 (Print)
Language
English
URI
http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?cmd=Retrieve&db=PubMed&dopt=Citation&list_uids=16425241

https://hdl.handle.net/10371/10866
DOI
https://doi.org/10.1002/jbm.a.30594
Files in This Item:
There are no files associated with this item.
Appears in Collections:

Altmetrics

Item View & Download Count

  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Share