Carbon supported, Al doped-Li3V2(PO4)(3) as a high rate cathode material for lithium-ion batteries

Cited 109 time in Web of Science Cited 113 time in Scopus
Authors
Cho, A. R.; Son, J. N.; Aravindan, V.; Kim, Heeran; Kang, Kisuk; Yoon, Woong Sup; Kim, W. S.; Lee, Yun-Sung
Issue Date
2012-03
Citation
Journal of Materials Chemistry, Vol.22 No.14, pp.6556-6560
Abstract
A high rate and high performance Li3V2(PO4)(3) cathode was prepared by applying a carbon coating and Al substitution using the conventional solid-state approach. X-Ray diffraction was used to observe the structural properties of the synthesized powders. The presence of the carbon coating was confirmed by HR-TEM and reflected well with the Raman analysis. The Li/C-Li3V1.98Al0.02(PO4)(3) cell displayed a discharge capacity of 182 mA h g(-1) between 3 and 4.8 V vs. Li at a current density of 0.1 mA cm(-1), which is similar to 20 mA h g(-1) higher than that of the native compound. The capacity retention was found to be 84 and 74% after 40 and 100 cycles, respectively. The C-Li3V1.98Al0.02(PO4)(3) powders demonstrated excellent rate performance at 20 C with a discharge capacity of similar to 120 mA h g(-1) over 100 cycles. The elevated temperature performance was also evaluated and found to be similar to that under room temperature conditions.
ISSN
0959-9428
URI
https://hdl.handle.net/10371/165140
DOI
https://doi.org/10.1039/c2jm00022a
Files in This Item:
There are no files associated with this item.
Appears in Collections:
College of Engineering/Engineering Practice School (공과대학/대학원)Dept. of Materials Science and Engineering (재료공학부)Journal Papers (저널논문_재료공학부)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse