Biomechanical and histological behavior of zirconia implants: an experiment in the rat
- Kohal, Ralf J.; Wolkewitz, Martin; Hinze, Marc; Han, Jung-Suk; Butz, Frank; Baechle, Maria
- Issue Date
- WILEY-BLACKWELL PUBLISHING, INC
- CLINICAL ORAL IMPLANTS RESEARCH, Vol.20, No.4, pp.333-339
- Objective: This study aimed at evaluating the integration of zirconia implants in a rat
Material and methods: Zirconia implants with two distinct surface topographies were compared with titanium implants with similar topographies. Titanium and zirconia
implants were placed into the femurs of 42 male Sprague–Dawley rats. Four groups of
implants were utilized: machined zirconia implants, zirconia implants with a rough surface,
machined titanium implants, and titanium implants with an electrochemically roughened
surface. After a healing period of 28 days, the load-bearing capacity between the bone and the implant surface was evaluated by a push-in test. Additionally, after a healing period of 14 and 28 days, respectively, bone tissue specimens containing the implants were processed and histologically analyzed.
Results: The mean mineralized bone-to-implant contact showed the highest values after 14
and 28 days for the rough surfaces (titanium: 36%/45%; zirconia: 45%/59%). Also, the pushin
test showed higher values for the textured implant surfaces, with no statistical
significance between titanium (34 N) and zirconia (45.8 N).
Conclusions: Within the limits of the animal investigation presented, it was concluded that all tested zirconia and titanium implant surfaces were biocompatible and osseoconductive.
The presented surface modification of zirconia implants showed no difference regarding the histological and biomechanical results compared with an established electrochemically modified titanium implant surface.