공초점 레이저주사현미경을 이용한 산부식 시간에 따른 법랑질 표면 양상에 관한 연구

Abstract

In order to evaluate the sufficient etching time for successful bonding and also minimizing unnecessary mineral loss, the enamel surface roughness analysis was performed using confocal laser scanning microscopy. Sixty extracted sound human molar teeth were imbedded in the center of acrylic cylinder using self-curing clear resin exposing buccal surface, and then polished with series of SiC paper(220, 500, 800, 1000, 2000, 4000 grit). Each specimen was randomly assigned to six groups(N=10). 37% phosphoric acid was applied to the polished tooth surface for 10, 20, 30, 40, 50, 60 seconds respectively and washed with copious water. After the surface roughness analysis, five roughness parameters(Sa, Sq, Sz, Sdr, Ra) were statistically analysed by ANOVA and Duncan post hoc test. We found that the all five parameters had higher roughness value in 30 seconds etching time, especially parameter Sz showed the lowest value in 10 seconds etching time and the highest value in 30 seconds etching time compared with the other etching times(p<0.05).