부하순환 하에서 제V급 복합레진 수복물의 미세변연누출에 대한 재접착제의 효과에 관한 연구

Abstract

One clinical technique recommended for improving marginal integrity is "rebonding" or application of unfilled resins to the surface of composite restoration. But continuously the restorations are affected with occlusal load. There is room for doubt that the rebonding agent has the positive effect on microleakage in spite of the stress generated by the occlusal load. This study determined the effect of rebonding on microleakage of Class V resin composite restorations under load cycling. Class V cavities were prepared on the buccal surface of 40 sound extracted premolars and restored with a hybrid light-cured resin composite according to manufacturers' directions. They were randomly divided into two groups consisting of 20 samples: a control(group I), without surface sealing, and the other group(group II) in which margins were etched and rebonded. After thermocycling, each of groups was divided into subgroups(group A, B), and load cycling(total 100,000 cycles with 4-100N load at a rate of 1 Hz) were applied on the group B. Assessment of microleakage utilized methylene blue dye penetration. The following results were obtained: 1. In the occlusal region, no significant difference was noted in the scores regardless of whether or not the rebonding agent was used(group TA-IIA, IB-IIB)(p>0.05). 2. In the cervical region, the control group with rebonding(group IIA) showed the better result than the group without rebonding(group IA)(p<0.05). 3. In the cervical region, the rebonded group with load cycling(group IIB) showed similar results to the group without rebonding(group IB) and no significant difference was noted(p>0.05).