치과용 콤포짓트 레진의 수분 흡수에 따른 압축강도와 굴곡강도의 변화에 관한 연구
- 정내정; 김정욱; 이상훈
- Issue Date
- 대한소아치과학회지 28(1):146-153, 2001.
- The difference of composition of composite resin may affect the mechanical properties of composite resin and the environment is important for the properties of materials. The composite resin restoration is always exposed to fluid in oral cavity and the composite resin matrix is able to absorb water, which is accompanied by some swelling of the composite The uptake of water by composites has been correlated with decreases in surface hardness and wear resistance. The purpose of this study was to investigate the effects of water storage in distilled water after 7days, 30days, 60days, 120days on compressive strength and flexural strength of dental composite resin, Z-100(group 1) Spectrum(group 2), Clearfil AP-X(group 3), Pyramid(group 4), Heliomolar(group 5). The compressive and flexural strength were measured by instron machine. The following results were obtained: 1. There were significant reduction of compressive strength as water storage time increased, 7days, 30days, 60 days, 120days(p<0.05). 2. There were significant reduction of flexural strength as water storage time increased, 7days, 30days, 60days, 120days(p<0.05). 3. Group 1, 2, 3 -hybrid type showed higher compressive and flexural strength than group 5-microfine type which had lower filler contents.