표면처리방법에 따른 복합레진의 결합강도에 관한 실험적 연구

Cited 0 time in Web of Science Cited 0 time in Scopus
Authors
신재호; 장기택; 한세현
Issue Date
1997
Publisher
대한소아치과학회
Citation
대한소아치과학회지, 24 : 112-124, 1997.
Keywords
air-abrasionacid etchingshear bond strength
Abstract
According to extensive use of composite resin which have superior esthetic property, every effort on improving bonding strength between a tooth and composite resin has been continued. Acid etching technique is a method that micro-etches the tooth surface which provides bonding with composite resin possible. Recently, there were several reports that mechanical treatment obtained from air-abrasion can provide similar bonding strength with acid etching technique. So, this experimental study was designed to compare the shear bonding strength between using air-abrasion technique and using acid etching technique. Initially, bovine teeth were divided into enamel and dentin experimental groups. Respectively each group was categorized into three subgroups. One subgroup was acid etched with 35% phosphoric acid, then bonded with composite resin. The other subgroup was air-abraded with particles sprayed with 160psi air pressure using air abrasion unit(KCP-1000, A.D.T., U.SA), and composite resin was bonded. In another subgroup, composite resin was bonded after acid etching following air-abrasion. So, enamel experimental groups were made of E1 (acid etched only), E2(air-abraded only), E3(acid etched following air-abraded), and dentin experimental groups were made of D1(acid etched only), D2(air-abraded only), D3(acid etched following air-abraded). Each subgroup had 10 specimens. Dentin bonding system(Scotchbond Multi-purpose, 3M Co., U.S.A.) and composite resin(Z-100, 3M Co., U.S.A.) were applied on treated surface using 5mm diameter gelatin capsule as manufacturer's direction. After 1200 times thermocycling between and , shear bond strength was measured in 5mm/min crosshead speed with Instron(Instron Co., U.S.A.), and also treated enamel and dentin were observed with SEM(JEOL Co., Japan). The following results were obtained: 1. In the enamel experimental groups, acid etched following air-abraded group had highest shear bond strength, but there was no significant difference compared to acid etched group. Air-abraded only group had lowest shear bond strength, and there was significant difference compared to the rest of groups. 2. In the dentin experimental groups, acid etched following air-abraded group had highest shear bond strength, but there was no significant difference compared to acid etched group. Air-abraded only group had lowest shear bond strength, and there was significant difference compared to the rest of groups. 3. In the SEM study, air-abraded enamel and dentin had irregular and rough surfaces.
ISSN
1226-8496
Language
Korean
URI
https://hdl.handle.net/10371/47875
Files in This Item:
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse