Collagenase와 esterase가 상아질 접착강도와 nanoleakage에 미치는 영향
- Issue Date
- 대한소아치과학회지, 35:389-398, 2008.
- The purpose of this study was to evaluate the effects of collagenase and esterase on dentin bond strength and nanoleakage. Resin composites were bonded to occlusal dentin of premolars with Single Bond 2(SB) and Clearfil SE Bond(SE). After the microtensile specimens were prepared and stored in PBS for 24 hours(I) or, PBS(II), collagenase(III), esterase(IV) solution for 4 weeks, the specimens were stained with silver nitrate solution. Microtensile bond strength() and silver penetration area were measured and, the results were as follows: 1. For group II, III, and IV, the bond strengths of SB were lower than those of SB(p<0.05). The bond strengths of SB II, III, and IV were lower than that of SB I(p<0.05). There was no difference among the bond strengths of SE groups(p>0.05). 2. Silver penetration areas of SB were higher than those of SE for all storage groups(p<0.05). In SB and SE groups, there was no significant difference of silver penetration area among groups(p>0.05). 3. SE I, II, and III showed inverse relationship between the bond strengths and the silver penetration areas(p<0.05).