Opalescence and fluorescence properties of indirect and direct resin materials
- Song, Sang-Hoon; Yu, Bin; Ahn, Jin-Soo; Lee, Yong-Keun
- Issue Date
- Taylor & Francis
- ACTA ODONTOLOGICA SCANDINAVICA 66: 4, 236-242
- Objective. To measure the opalescence and fluorescence properties of indirect and direct resin materials before and after polymerization, and to determine the influence of the material and shade group combination on these properties. Material and methods. BelleGlass NG (BG, indirect resin) and Estelite Sigma (ES, direct resin), each composed in 3 shade groups (EN, OD and TL for BG; BS, AS and OP for ES) out of a total of 16 shades were investigated. Resin material was packed into a mold (the BEC condition) and polymerized with a light-polymerization unit (CWL). Secondary polymerization (CIC) was performed for BG. Color was measured in the BEC, CWL, and CIC conditions, and the opalescence parameter (OP) and fluorescence parameter (FL) were calculated. Results. For the OP, the mean for BG material was 24.3 before polymerization, which changed to 19.9 after polymerization (CIC). In the case of ES, the mean OP before polymerization was 25.6, which changed to 12.4 after polymerization (CWL). For the FL, the mean FL for BG was 2.5 before polymerization, which changed to 0.7 after polymerization. In the case of ES, the mean FL before polymerization was 1.2, which did not change after polymerization. Material and shade group combination influenced the OP and FL values (p<0.05). Conclusions. The opalescence and fluorescence properties of resin materials varied depending on the material, shade group, and polymerization. Clinically, these properties should be considered when neighboring teeth are restored with different types of material.
- Files in This Item: There are no files associated with this item.