나노컴포지트에서 Acidulated Phosphate Fluoride 적용에 따른 Streptococcus mutans 부착량 변화
Changes in adhesion of Streptococcus mutans to nanocomposite resins after acidulated phosphate fluoride gel applicaion

Cited 0 time in Web of Science Cited 0 time in Scopus
Authors
정영정; 김영재; 김정욱; 장기택
Issue Date
2005-08
Publisher
대한소아치과학회
Citation
J Korean Acad Pediatr Dent 32:427-436, 2005
Keywords
나노충전재Streptococcus mutans 부착표면조도NanofillerAPF gelStreptococcus mutans adhesionSurface roughness
Abstract
복합레진 표면에 대한 APF gel 도포는 표면을 거칠게 하고 세균 부착을 증가시킨다. 본 연구는 Filtek Z250(FZ), Filtek Supreme Universal(FS)과, 실험적으로 나노충전재를 각각 0%, 3%, 6% 포함시켜 만든 복합레진(E0, E3, E6)으로 제작한 레진 시편을, APF gel을 적용한 군과 적용하지 않은 군으로 나누어 Streptococcus mutans의 부착량과 표면 조도를 측정하고 비교, 평가하여 다음과 같은 결과를 얻었다. 1. APF gel을 적용하지 않은 레진 시편에 대한 S. mutans 부착량은 FS에서 가장 적었고, FZ, E3, E6에 대한 부착량보다는 유의하게 낮았다(p<0.05). 2. 모든 레진군에서 APF gel을 적용한 레진 시편에 대한 S. mutans 부착량은 APF gel을 적용하지 않은 시편에 대한 부착량보다 유의하게 높았다(p<0.05). 3. APF gel을 적용한 레진 시편에 대한 S. mutans 부착량은 레진군간 유의한 차이를 보였으며(p<0.05), FS, FZ, E0, E3, E6의 순서로 높은 값을 보였다. 4. APF gel 적용 전이나 후에, 레진군간 표면조도의 차이는 유의하지 않았다(p>0.05).
Topical application of APF gel can increase the surface roughness of resin composites and the roughened surfaces may allow increased bacterial accumulation and surface staining. Resin specimens of two proprietary resin composites, Filtek Z250(FZ) and Filtek Supreme Universal(FS), and experimental resin composites containing 0%, 3%, 6% nanofillers(E0, E3, E6) were fabricated and divided into two groups of the same number; APF treatment group and no treatment group. The amount of S. mutans adhered to specimens and the mean surface roughness(Ra) were measured. The results were as follows; 1. In no treatment group, the amount of S. mutans adhered to FS was the smallest. It was significantly different from those of FZ, E3, E6(p<0.05) although it was not significantly different from that of E0(p>0.05). 2. For all resin composites used, the amount of S. mutans adhesion in APF treatment group was significantly greater than that in no treatment group(p<0.05). 3. In APF treatment group, the amount of S. mutans adhesion was significantly different between materials(p<0.05), and increased in order of FS, FZ, E0, E3 and E6. 4. Difference of the surface roughness(Ra) between materials was not statistically significant in both no treatment group and APF treatment group(p>0.05).
ISSN
1226-8496
Language
English
URI
https://hdl.handle.net/10371/73997
Files in This Item:
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse