The effect of Er:YAG laser irradiation on the scanning electron microscopic structure and surface roughness of various implant surfaces: an in vitro study

Cited 0 time in Web of Science Cited 0 time in Scopus
Authors
Shin, Seung-Il; Min, Hyung-Ki; Park, Bo-Hyun; Kwon, Young-Hyuk; Park, Joon-Bong; Herr, Yeek; Heo, Seong-Joo; Chung, Jong-Hyuk
Issue Date
2010-08
Publisher
Springer Verlag
Citation
Lasers in Medical Science (2010)1-10
Keywords
Er:YAG laserImplant surface alterationSLASurface roughnessTi-Unite®
Abstract
The purpose of this study was to evaluate the surface roughness (Ra) and microscopic change to irradiated dental implant surfaces in vitro and ultimately to determine the proper pulse energy power and application time for the clinical use of Er:YAG lasers. Anodic oxidized surface implants and sand-blasted, large-grit, and acid-etched (SLA) surface implants were used. Each experimental group of implant surfaces included ten implants. Nine implants were used for the laser irradiation test groups and one for the control group. Each test group was equally divided into three subgroups by irradiated pulse energy power. Using an Er:YAG laser, each subgroup of anodic oxidized surface implants was split into 60-, 100-, and 140-mJ/pulse groups, with each subgroup of SLA surface implants irradiated with a 100-, 140-, or 180-mJ/pulse. Three implants in every test subgroup were respectively irradiated for 1, 1.5, and 2 min. The Ra values for each specimen were recorded and every specimen was observed by SEM. Irradiation by Er:YAG laser led to a decrease in implant surface roughness that was not statistically significant. In anodic oxidized surfaces, the oxidized layer peeled off of the surface, and cracks appeared on implant surfaces in the 100- and 140-mJ/pulse subgroups. However, with SLA surfaces, no significant change in surface texture could be found on any implant surface in the 100- and 140-mJ/pulse subgroups. The melting and fusion phenomena of implant surfaces were observed with all application times with 180 mJ/pulse irradiation. The SLA implant surfaces are stable with laser intensities of less than 140 mJ/pulse and an irradiation time of less than 2 min. The anodic oxidized surfaces were not stable with laser intensities of 100 mJ/pulse when an Er:YAG laser was used to detoxify implant surfaces.
ISSN
0268-8921
Language
English
URI
https://hdl.handle.net/10371/74180
Files in This Item:
There are no files associated with this item.
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse