Cited 5 time in Web of Science Cited 5 time in Scopus
Authors
Lim, Ho-Nam; Yu, Bin; Ahn, Jin-Soo; Lee, Young-Keun; Lim, Jin Ik
Issue Date
2009-12
Publisher
ELSEVIER SCI LTD
Citation
MATERIALS & DESIGN, Vol.30, No.10, pp.3996-4002
Keywords
OpticalGlass ionomerComposites polymer matrix
Abstract
The influence of 2-hydroxyethyl methacrylate (HEMA) on the properties of HEMA-added dental glass ionomer (HAGI) should be determined systematically to develop a smart restorative material. The purposes of this study were to determine the influence of incrementally added HEMA in experimental HAGIs on the color, translucency, opalescence, fluorescence and compressive strength, and to compare with those of commercial resin-modified glass ionomer (RMGI) materials. A varied amount of HEMA (1050 wt.%) was added into commercial glass ionomer liquid (Fuji II), which was then mixed with three shades of the same glass ionomer powder (shade nos. 21, 22 and 23). RMGIs from the same manufacturer were also investigated. Five specimens, 10 mm in diameter and 2 mm in thickness, were fabricated for each condition. Color of the HAGIs and RMGIs was measured with a reflectance spectrophotometer in the reflectance and the transmittance modes. Translucency, opalescence and fluorescence parameters were calculated. Compressive strength was determined. As the HEMA content increased, CIE L* value (lightness) decreased while the chroma increased. CIE a* value showed small and CIE b* value showed high increase as the HEMA content increased. Increase in translucency was generally dependent on HEMA content except for 30% HEMA condition of shade no. 21. Opalescence decreased as the HEMA content increased while the trend of fluorescence change was shade-dependent. Compressive strength significantly increased after HEMA addition except 50% HEMA condition. The influence of HAMA on the optical properties of HAGIs varied by the shade of powder and the amount of HEMA For the most relevant simulation of the optical properties of teeth, addition of 30-40% HEMA is recommended when formulating HEMA- added glass ionomers. (C) 2009 Elsevier Ltd. All rights reserved.
ISSN
0261-3069
Language
English
URI
https://hdl.handle.net/10371/80388
DOI
https://doi.org/10.1016/j.matdes.2009.05.027
Files in This Item:
There are no files associated with this item.
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse