The effect of preparation order on the crystal structure of yttria-stabilized tetragonal zirconia polycrystal and the shear bond strength of dental resin cements

DC Field Value Language
dc.contributor.authorMoon, Ji-eun-
dc.contributor.authorKim, Sung-hun-
dc.contributor.authorLee, Jai-bong-
dc.contributor.authorHa, Seung-ryong-
dc.contributor.authorChoi, Yu-sung-
dc.date.accessioned2013-01-22T01:28:24Z-
dc.date.available2013-01-22T01:28:24Z-
dc.date.issued2011-
dc.identifier.citationDental Materials, Vol.27, No.7, pp.651-663ko_KR
dc.identifier.issn0109-5641-
dc.identifier.urihttps://hdl.handle.net/10371/80917-
dc.description.abstractObjectives. The purpose of this study was to evaluate the effect of preparation order on the crystal structure of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and the shear bond strength of dental resin cements.
Methods. One-hundred fifty pre-sintered Y-TZP cylinders (Ø 9mm×13.5mm) were prepared
and divided into three groups (control group, SBS group and SAS group). Specimens in control group were not treated. Specimens in SBS group were sandblasted and then densely
sintered, and specimens in SAS group were sintered in advance, and then sandblasted.
The specimens were analyzed by X-ray diffractometry, confocal laser scanning microscopy and Energy dispersive X-ray spectroscopy before and after sandblasting. All specimenswere embedded in polytetrafluoroethylene (PTFE) molds using PMMA and each group was divided into five subgroups. The mixed resin cements (Clearfil SA luting cement, Zirconite, Superbond C&B, Rely-X Unicem, and Multilink) were placed onto the Y-TZP surfaces using PTFE molds with Ø 3mm×3mm, followed by storage in distilled water at 37 ◦C for 24 h, and thermocycling
(5000 cycles at 5 ◦C and 55 ◦C with a 30 s dwelling time). All specimens were tested
for the shear bond strengths with a universal testing machine, and fractured surfaces were
evaluated by SEM. Statistical analysis was performed using one-way ANOVA and Scheffé
comparison with ˛ = .05.
Results. Sandblasting of the zirconia significantly increased shear bond strength of resin cements, but the preparation order had no significant influence on the shear bond strength in both test groups. In SEM observation, the natures of the surface faceting of the zirconia grains were totally different between SBS and SAS groups. SBS group exhibited less monoclinic structures than SAS group.
Significance. Sandblasting of pre-sintered Y-TZP and then sinteringmay induce favorable proportion of tetragonal structures. This might have positive effect on the clinical performance of zirconia restorations. © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
ko_KR
dc.description.sponsorshipThis study was supported by the research grant No. 03- 2009-0017 from the Seoul National University Dental Hospital
Research Fund.
The Y-TZP ceramic materials (Rainbow, Dentium, Seoul, Korea) used in this study were generously supplied by their manufacturers.
ko_KR
dc.language.isoenko_KR
dc.publisherElsevierko_KR
dc.subjectResin cementko_KR
dc.subjectZirconiako_KR
dc.subjectShear strengthko_KR
dc.subjectY-TZP ceramicko_KR
dc.titleThe effect of preparation order on the crystal structure of yttria-stabilized tetragonal zirconia polycrystal and the shear bond strength of dental resin cementsko_KR
dc.typeArticleko_KR
dc.contributor.AlternativeAuthor문지은-
dc.contributor.AlternativeAuthor김성훈-
dc.contributor.AlternativeAuthor이재봉-
dc.contributor.AlternativeAuthor하승룡-
dc.contributor.AlternativeAuthor최유성-
dc.identifier.doi10.1016/j.dental.2011.03.005-
dc.citation.journaltitleDental Materials-
dc.description.tc2-
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
Files in This Item:
There are no files associated with this item.
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse