Evaluation of deposited silicon oxide with post-deposition annealing for gate oxide of MOS capacitors on 4H-SiC
Cited 0 time in
Web of Science
Cited 0 time in Scopus
- Authors
- Advisor
- 김형준
- Major
- 공과대학 재료공학부
- Issue Date
- 2018-02
- Publisher
- 서울대학교 대학원
- Keywords
- 4H-SiC ; MOS capacitor ; PEALD ; sputtering ; post-deposition annealing
- Description
- 학위논문 (박사)-- 서울대학교 대학원 : 공과대학 재료공학부, 2018. 2. 김형준.
- Abstract
- Silicon carbide (SiC) is one of the promising materials being developed for the application of power devices. The 4H-SiC metal-oxide-semiconductor field effect transistors (MOSFETs) using 4H-SiC as substrate are expected to play a major role as a power semiconductor device. However, carbon clusters, which are formed in the oxidation process, increase interface states, and thus deteriorate device performance. Many researches have reported that the efficient method to remove the interfacial traps is the post-oxidation annealing (POA) using nitric oxide (NO) gas, which has become common process to remove interface traps. Although NO POA is effective on reducing interface traps, it is necessary to find the alternative and advanced methods to reduce interface traps effectively: deposition is one of them, because the most of carbon clusters are formed during oxidation process. The deposition of oxide films has been usually carried out by chemical vapor deposition (CVD) and atomic layer deposition (ALD). ALD oxide with NO post-deposition annealing (PDA) showed excellent performance was reported, but the MOSFET, which was fabricated with the ALD oxide, consisted of thin oxide less than 30 nm. However, the commercial products commonly used thicker than 50 nm. In this dissertation, oxide films thicker than 40 nm were deposited by ALD or sputtering, and then MOS capacitors were fabricated to evaluate their electrical and physical properties. And the effects of PDA conditions on the deposited oxide were also investigated. In addition, to evaluate the feasibility of oxide deposition without PDA, the oxides, which were deposited on the thermal buffer oxide, were also investigated.
In order to densify the 50 nm SiO2 oxide film deposited with plasma-enhanced ALD (PEALD), the PDA was performed using Ar gas, which is an inert gas. At this time, the PDA was operated at 400, 600, 800, 1000, and 1200°C for 2 h. HF etch test and leakage current analysis showed that the oxide film was stabilized after densifying at 1000°C or higher. However, in the capacitance‒voltage (C‒V) characteristics, the densified sample at 1000°C was found to be in a less stable state, but a stable oxide film was formed only at 1200°C. In addition, the NO PDA, known to be effective at 30 nm, was conducted for 2 h at 1200°C on PEALD oxide. The C‒V hysteresis decreased significantly compared to the as-dep oxide, but the flat-band voltage (VFB) shifted significantly in the negative direction. This is because the thicker the oxide film, the greater the positive charging by nitrogen atoms.
On the other hand, sputtering is a traditional physical vapor deposition (PVD) method, but it has not been often used to deposit the gate insulating films. To evaluate whether this sputtering SiO2 oxide film can be used as an insulating film, MOS capacitors with sputtered oxide were fabricated and their electrical properties and physical properties were also analyzed. N2, NH3, O2, and NO PDA were conducted to stabilize the sputtered oxide. All the samples were found to be sufficiently densified through refractive index measurement and HF etching test, and in the case of O¬2 PDA, an additional oxidation reaction occurred. As a result of the insulation property evaluation, N2 and NH3 did not have good insulation characteristics, which seems to be the result of the chemical reaction of nitrogen, increasing the leakage current. In the case of O2 and NO, they showed insulation characteristics but it was insufficient compared to thermal oxide. For the optimization of NO PDA for sputtering oxide, the 30, 60, and 90 min of NO PDAs were also investigated. As PDA time increased, VFB was negatively shifted and hysteresis decreased. As a result of normalized conductance‒frequency (GP‒ω) and Dit characteristics, the lowest interface traps were shown in the 60 min NO PDA among three conditions.
Since both PEALD and sputtering use plasma, it is necessary to judge whether the plasma damage affects the substrate and interface characteristics. A passivation layer was formed through pre-oxidation before deposition, and then an oxide film was formed through PEALD and sputtering. As-deposition oxide without PDA showed poor insulating properties and large leakage current. However, pre-oxidation greatly reduced the leakage current and allowed a normal C‒V curve to be obtained. Although the leakage current is not as good as that of the thermal oxide, the overall characteristics are sufficiently improved for both PEALD and sputtering oxide. Based on these results, pre-oxidations using NO and N2O were conducted, and showed superior C‒V characteristics when using N2O and NO/O2 mixed gas.
In this dissertation, whether the deposition SiO2 can be used as the gate oxide was investigated. To improve characteristics of PEALD and sputtering SiO2, post-deposition annealing and pre-oxidation were conducted. The applicability of PEALD and sputtering oxide was investigated through PDA and pre-oxidation under various conditions. If the deposition and annealing conditions were optimized, deposition oxide will have competitive enough to be used as a gate oxide for 4H-SiC MOS device.