Origin of the Mixing Ratio Dependence of Power Conversion Efficiency in Bulk Heterojunction Organic Solar Cells with Low Donor Concentration

Abstract

We studied the origin of the improvement in device performance of thermally evaporated bulk heterojunction organic photovoltaic devices (OPVs) with low donor concentration. Samples with three different donor-acceptor mixing ratios, 0:10 (C-70-only), 1:9 (low-doped) and 3:7 (high-doped), were fabricated with 1,1-bis-(4-bis(4-methyl-phenyl)-amino-phenyl)-cyclohexane (TAPC):C-70. The power conversion efficiencies (PCEs) of these samples were 1.14%, 2.74% and 0.69%, respectively. To determine why the low-doped device showed a high PCE, we measured various properties of the devices in terms of the effective energy band gap, activation energy, charge carrier mobility and recombination loss. We found that the activation energy for charge carrier transport was increased as we increased the TAPC concentration in the blends whereas the hole and electron mobilities became more balanced as the TAPC concentration was increased. Furthermore, the recombination loss parameter alpha (from the light intensity dependence) remained alpha similar to 0.9 in the low-doped device, but it decreased to alpha similar to 0.77 in the high-doped device, indicating a large recombination loss as a result of space charge. Therefore, the improved PCE of low-doped OPVs can be attributed to the balance between carrier mobilities with no increase in recombination loss.