수종의 실란처리 유리섬유를 첨가한 의치상용 레진의 강도변화 및 마모전.후 표면성상분석
EFFECTS Of VARIOUS SILANE COUPLING AGENTS ON THE STRENGTH AND THE SURFACE ROUGHNESS OF GLASS FIBER-ADDED PMMA RESIN

Cited 0 time in Web of Science Cited 0 time in Scopus
Issue Date
2007
Publisher
대한치과보철학회
Citation
2007;45:4
Keywords
Glass fiberSilanePMMA resinSurface roughnessTransverse strength
Abstract
Statements of problem: The fracture of acrylic resin dentures remains an unsolved problem. Therefore, many investigations have been performed and various approaches to strengthening acrylic resin, for example, the reinforcement of heat-cured acrylic resin using glass fibers, have been suggested over the years. Silane is important for bonding between glass fiber and resin. Purpose: The aim of the present study was to investigate the effect of various silane on the strength of PMMA resin and roughness of resin-glass fiber complex after abrasion test. Material and methods: 3mm glass fiber (Chopped strand, Hankuk fiber Co., Milyang, Korea) was treated with 3 kinds of silane (MPS, EPS, APS) (Sila-ace, Chisso chemical, Tokyo, Japan) and mixed with PMMA resin(Vertex RS, Vertex Dental B.V., Zeist, Netherlands). Transverse strength and Young's modulus was measured using Instron (Instron model 4466, Instron, Massachusetts, USA). After abrasion test (The 858 Mini Bionix II Test System, MTS System Co., Minnesota, USA) surface roughness was evaluated using tester (Form Talysurf plus, Taylor Hopson Ltd., Leicester England). Examination of scanning electron microscope was also performed. Results: Within this study, the following conclusions were drawn. 1. Surface treatment of glass fiber with MPS and APS increased transverse strength of PMMA resin complex, but surface treatment with EPS decreased transverse strength of PMMA resin complex (p<0.05). 2. Silane treated glass fiber increased Young's modulus of PMMA resin complex compared to desized glass fiber (p<0.05). 3. Roughness increased after abrasion test in case of PMMA resin reinforced with desized glass fiber (p<0.05). 4. Roughness change was not observed after abrasion test in case of PMMA resin reinforced with silane treated glass fiber (p>0.05).
ISSN
0301-2875
Language
Korean
URI
https://hdl.handle.net/10371/47434
Files in This Item:
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse