산화 티타늄 블라스팅 임프란트 표면구조에 대한 염산 테트라싸이클린의 영향
Micromorphometric change of TiO₂blast implant surface conditioned with tetracycline-HCI

Cited 0 time in Web of Science Cited 0 time in Scopus
Authors
이정민; 허익; 권영혁; 박준봉; 정종혁; 허성주
Issue Date
2007
Publisher
대한치주과학회
Citation
대한치주과학회지 2007;37:599-611.
Keywords
TiO₂blast implant surfacetetracyclina-HCIdetoxification
Abstract
The present study was performed to evaluate the surface roughness and effect of Tetracycline-HCI on the change of implant surface microstructure according to application time. TiO₂ surface Implant was utilized. Implant surface was rubbed with 50mg/ml Tetracycline-HCI solution for 0.5min, 1min, 1.5min, 2min, 2.5min and 3min respectively in the Tetracycline-HCI group. Then, specimens were measured surface roughness and processed for scanning electron microscopic observation. The results of this study were as follows. 1. TiO₂ blast implant surface showed increased surface roughness 1.5 minute after treatment with Tetracycline-HCI. But, there were not significant differences in saline group after treatment. 2. Tetracycline-HCI group showed changed surface micro-morphology in SEM after 1.5 minute. There were not significant differences in saline group after treatment. 3. Between Tetracycline-HCI group and saline group, there were difference in surface roughness change and SEM micro-morphology. Tetracycline-HCI have influence on TiO₂ blast implant surface. In conclusion, the detoxification with 50mg/ml Tetracycline-HCI must be applied respectively with different time according to various implant surfaces.
ISSN
0250-3352
Language
Korean
URI
https://hdl.handle.net/10371/47720
Files in This Item:
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse