중합시간과 중합방법에 따른 자가중합형 상교정용 레진의 중합률의 비교에 관한 연구

Cited 0 time in Web of Science Cited 0 time in Scopus
Authors
유종욱장기택김종철
Issue Date
1999
Publisher
대한소아치과학회
Citation
대한소아치과학회지 26:296-309, 1999.
Keywords
autopolymerized resinFourier Transform Infared spectroscopyheat cured resinpolymerizationunreacted monomer
Abstract
Autopolymerized resin facilitates a more rapid and easier means for the construction of removable orthodontic appliances than heat cured resin. But many reports reveal that more unreacted monomer is found in autopolymerized resin. It is very important to achieve maximum degree of polymerization because if polymerization is inadequate, high level of unreacted monomer has been shown to adversely affect mechanical and physical properties, and also the question of allergy or toxicity to methylmethacrylate must be considered. The purpose of this study was to compare the degree of polymerization according to curing method and curing time. Five groups were desinged ; Group 1 was polymerizied at room temperature() ; Group 2 in water ; Group 3 in water under 30psi pressure ; Group 4 in water ; Group 5 in water under 30psi pressure for 10 minutes, 1 hour 12 hours, 1 day and 3 days. The degree of polymerization was measured by means of Fourier Transform Infrared spectroscopy. The results were as follows: 1. The degree of polymerization increased constantly in accordance with curing time in all groups and after curing for 10 minutes, Group 1 showed significantly higher degree of polymerization after 12 hours and Group 2, Group 3, Group 4, Group 5 after 1 hour(p<0.05). 2. The degree of polymerization decreased in the order of Group 5, Group 4, Group 3, Group 2, Group 1 except when the curing time was 1 hour and 12 hours(p<0.05). 3. The degree of polymerization of Group 4, Group 5 cured at showed significantly higher degree of polymerization than Group 2, Group 3 at except when the curing time was 1 day(p<0.05). 4. Among Group 2, Group 3 and Group 4, Group 5, the pressure had no effect on polymerization except when the curing time was 12 hours(p<0.05). 5. Between Group 1 and Group 2, the method of storage had no effect on polymerization except when the curing time was 1 hour(p<0.05).
ISSN
1226-8496
Language
Korean
URI
https://hdl.handle.net/10371/47818
Files in This Item:
Appears in Collections:
College of Dentistry/School of Dentistry (치과대학/치의학대학원)Dept. of Dentistry (치의학과)Journal Papers (저널논문_치의학과)
  • mendeley

Items in S-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

Browse